Rumah > Produk >

Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds

Name: Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds
Brand: Shenzhen Hanast New Material co.,LTD
SKU: HN-620 A/B.
Availability: InStock

Detail Produk:

Tempat asal:	Guangdong, Tiongkok
Nama merek:	Hanast
Sertifikasi:	ROHS，SGS
Nomor model:	HN-620 A/B.

Informasi Rinci

Tempat asal:

Guangdong, Tiongkok

Nama merek:

Hanast

Sertifikasi:

ROHS，SGS

Nomor model:

HN-620 A/B.

Nilai:

Kelas makanan

Fitur:

Ramah Lingkungan

Warna:

Transparan

Membentuk:

Cairan dua komponen

Aplikasi:

Pembuatan cetakan

Penampilan:

Cairan dua komponen

Kekerasan:

35 pantai

Umur Simpan:

12 bulan pada suhu kamar (di bawah 25C)

Informasi Perdagangan

Kuantitas min Order:

1 kilogram

Harga:

Dapat dinegosiasikan

Kemasan rincian:

25kg/drum besi

Waktu pengiriman:

5-7 hari

Syarat-syarat pembayaran:

T/T

Deskripsi Produk

It is extensively applied in mold manufacturing for multiple industries, including food-grade molds, resin crafts, gypsum artworks, handmade soap molds, tire replica molds and various split casting molds.Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds

Product Description :

Tin-cured liquid silicone rubber, also referred to as condensation-type liquid silicone rubber, is a two-part system consisting of Component A and Component B with a standard mixing weight ratio of 100:2. It features room-temperature curing capacity, hence named RTV silicone rubber.

Specification

Model	HN-620AB	HN-630AB
Color	white/translucent	white/translucent
Viscosity (cs)	18000-25000	18000-25000
Gravity ( G/cm 3 )	1.06	1.06
Hardness(A°)	20	30
Strength( MPa)	3.1-3.6	3.4-4.1
Tear Strength (kN/m )	19.8-24.3	19.8-23.4
Elongation(%)	600-720	560-630
Linear Shrinkage(%)	≤0.2	≤0.2
Curing Agent Addition Ratio(%)	2-3%	2-3%
Operating Time( mins )	30-40	30-40
Curing Time( hours )	3-4	3-4

Application:

1. Two-part system: liquid silicone base matched with curing agent

2. Excellent fluidity for bubble-free pouring and easy casting operation

3. Outstanding heat resistance, acid & alkali resistance, plus ultra-low shrinkage rate

4. High tensile strength and superior tear resistance, supporting repeated mold replicatio

operate:

Thoroughly shake Component B (curing agent) before use. Weigh Component A and B strictly at a 100:2 weight ratio, then stir the mixture uniformly. Be sure to scrape the container’s bottom and side walls repeatedly to achieve full blending of silicone and curing agent. Complete and even mixing is mandatory; incomplete mixing will shorten the service life of silicone molds.

Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds 0

Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds 1

Tag:

Condensation Cure Liquid Silicone Rubber Low Shrinkage One To One Ratio For Sculpture Casting Molds

silikon penyembuh timah,

LSR Silikon,

silikon cair untuk cetakan

MSDS Karet Silikon Cair RTV Siloczest Untuk Pembuatan Cetakan 1KG

Bulk RTV 2 Tin Cure Silicone Rubber Liquid Untuk Cetakan Cornice Plaster

20kg Momentive Liquid Transparent Silicone Rubber RTV-2 FDA Disetujui

Dua Bagian RTV2 Tin Cure Silikon Karet Cairan Untuk Tuang Sikat Injeksi Molding

HN-620 A/B Karet Silikon Cair Penyusutan Rendah untuk Pembuatan Kerajinan Cetakan Injeksi

1002 Industri Momentive Tin Cure Karet Silikon Karet Cair Untuk PU Resin Mold

RTV2 Tin Cured LSR Silicone Rubber Cairan Semi Transparan untuk Pengecoran Pembuatan Cetakan 200kg