Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone

Name: Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone
Brand: Shenzhen Hanast New Material co.,LTD
SKU: HN-630
Availability: InStock

Λεπτομέρειες προϊόντος:

Τόπος καταγωγής:	Guangdong, Κίνα
Μάρκα:	Hanast
Πιστοποίηση:	ROHS
Αριθμό μοντέλου:	HN-630

Λεπτομέρειες

Τόπος καταγωγής:

Guangdong, Κίνα

Μάρκα:

Hanast

Πιστοποίηση:

ROHS

Αριθμό μοντέλου:

HN-630

Επισημαίνω:

High Light

Επισημαίνω:

Cement Cultural Stone Molds Silicone Rubber

High Tear Resistance Silicone Rubber

Tin Cured Liquid Silicone Rubber

Πληροφορίες συναλλαγών

Ποσότητα παραγγελίας min:

1 κιλό

Τιμή:

USD

Συσκευασία λεπτομέρειες:

25kg/βάρελ

Χρόνος παράδοσης:

5-8 ημέρες

Όροι πληρωμής:

D/P, D/A, T/T

Περιγραφή του προϊόντος

Condensed Mold Silicone 100:2 Tin Cured Liquid Silicone Rtv 2 Molding Silicone Rubber For Resin Mold Handicraft Indutry Gypsum

Product description:

The main components of condensed silicone rubber mold liquid include: polysiloxane (raw rubber) with hydroxyl end groups and partial side groups, fillers, crosslinking agents, and vulcanization accelerators.
The main components of addition molded silicone rubber include: polysiloxane (raw rubber) with vinyl end groups and some side groups, hydrogen containing silicone oil (crosslinking agent), platinum catalyst (catalyst), and white carbon black (filler).

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 0

Application:

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 1

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 2

Model	HN-620AB	HN-630AB
Color	white / translucent	white / translucent
Viscosity (cs)	18000-25000	18000-25000
Gravity ( G/cm 3 )	1.06	1.06
Hardness(A°)	20	30
Strength( MPa)	3.1-3.6	3.4-4.1
Tear Strength (kN/m )	19.8-24.3	19.8-23.4
Elongation(%)	600-720	560-630
Linear Shrinkage(%)	≤0.2	≤0.2
Curing Agent Addition Ratio(%)	2-3%	2-3%
Operating Time( mins )	30-40	30-40
Curing Time( hours )	3-4	3-4

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 3

The operational time and demolding time after the ratio of silicone and curing agent:
When the amount of curing agent added is 1%, the colloid will still flow after 2.5 hours and can be demolded after 6-8 hours;
When the amount of curing agent added is 2%, the colloid will still flow within 50-1 hour, and demolding can be carried out within 2-3 hours;
When the amount of curing agent added is 3%, the colloid will still flow after 28 to 30 minutes, and demolding can be carried out after 1.5 to 2 hours;
When the amount of curing agent added is 4%, the colloid will still flow within 10-15 minutes and can be demolded within 1-1.5 hours.

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 4

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 5

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 6

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 7

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone 8

Ετικέτες:

Tin Cured Liquid Silicone Rubber 100:2 For Cement Cultural Stone Molds High Tear Resistance Liquid Silicone

High Light

Επισημαίνω:

Cement Cultural Stone Molds Silicone Rubber

High Tear Resistance Silicone Rubber

Tin Cured Liquid Silicone Rubber

Σιλικόνη στεγνώσεως τσιμέντου,

Σιλικόνη LSR,

υγρό σιλικόνης για μούχλες

MSDS RTV Siloczest υγρό καουτσούκ σιλικόνης για μούχλες που παράγουν 1KG

Χύδης RTV 2 Τήνιο θεραπεία Σιλικόνη υγρό καουτσούκ για το γύψο σχήματα κορνίς

20 κιλά Momentive Διαφανές υγρό καουτσούκ σιλικόνης RTV-2 Εγκρίθηκε από το FDA

Δύο μέρη RTV2 Tin Cure Silicone Rubber υγρό για χύσιμο βούρτσισμα Σφουγγαρισμός

Χαμηλή συρρίκνωση Τσιμένιο θεραπεία υγρού σιλικόνης Ένεση Μούλντινγκ καουτσούκ Εργασίες κατασκευής HN-620 A / B

1002 Βιομηχανική κινητική κασσίτερος σιδηρουργική καουτσούκ υγρό καουτσούκ για πλυντήριο ρητίνης PU

RTV2 Χύδης από κασσίτερο LSR Σιλικόνιο καουτσούκ ημιδιαφανές υγρό για την κατασκευή καλούπιων 200kg