55 Shore A cured Silicone Potting Compound Glue Adhesive 1:1 2 Parts

All Category

Tin Cure Silicone Rubber

Platinum Cure Silicone Rubber

Clear Liquid Silicone

Food Safe Liquid Silicone

Electronic Silicone Gel

Squishy Silicone Gel

Silicone Potting Compound

Epoxy Potting Compound

Polyurethane Potting Compound

Thermally Conductive Potting Compound

Silicone Pigment

Degumming Agent

Ms. Candy

sales11@hanastsilicone.com/candy@hanastsilicone.com

+8613670122311

13670122311

Contact Now

55 Shore A cured Silicone Potting Compound Glue Adhesive 1:1 2 Parts

Brand Name:	Hanast
Model Number:	HN-8806 A/B (1:1)
MOQ:	1 Kilogram
Price:	Negotiable
Packaging Details:	25KG/ Iron Drum
Payment Terms:	T/T

Detail Information

Product Description

Detail Information

Place of Origin:

Guangdong, China

Certification:

ROHS，SGS

Color:

Grey,white, Black (can Be Customized)

Hardness::

50±5 Shore A

Mix Ratio:

Waterproof:

Material:

Silicone

Type:

2 Parts(A And B)

Sample:

1-2kgs

Application:

Electronic Components

Feature:

Flame Retardant, High And Low Temperature Resistance

Thermal Conductivity:

≥0.76w/m·k(can Be Customized)

Highlight:

Silicone Potting Compound Glue

cured Silicone Potting Compound

2 Parts Silicone Potting Glue

Product Description

55 Shore A Silicone Potting Glue 1:1 2 Parts Potting Compound Waterproof High Thermal Conductivity Potting Adhesive For Circuit Board Led Module Power

HN-8806 A/B (1:1)

PRODUCT DESCRIPTION

HN-8806, two-component addition type silicone potting rubber which can be cured into high-performance elastomer by room temperature or heating.

This potting silicone rubber has excellent electrical insulation, high moisture resistance, and a wide temperature range of -50°C to 250°C.

Technical Parameters:

		Test Items	Test Standard	Units	Product test results
		Test Items	Test Standard	Units	Part A	Part B
Before Curing	1	Appearance	By eyes	---	Grey, fluid	White, fluid
	2	Viscosity	GB/T10247- 2008	25ºC,mPa·S	4500~5000	4500~5000
	3	Density	GB/T 13354-92	25ºC,g/cm3	1.50±0.05	1.50±0.05
	4	Mixing Ratio (A : B)	1:1	Weight ratio	100	100
	4	Mixing Ratio (A : B)	1:1	Volume ratio	100	100
	5	Operating time	Measured	hr	0.3-0.4
	6	Curing condition	Measured	hr	4~12 (25ºC, initial cure)
	6	Curing condition	Measured	hr	0.20 (80ºC)
After Curing	7	Appearance	By eyes	---	Grey Elastomer
	8	Hardness	GB/T 531.1-2008	Shore A	50±5
	9	Thermal conductivity	GB/T10297-1998	w/m·k	≥0.76
	10	Expansivity	GB/T20673-2006	µm/(m,ºC)	210
	11	Moisture Absorption	GB/T 8810-2005	24h,25ºC,%	0.01~0.02
	12	Volume resistivity	GB/T 1692-92	(DC500V),Ω· cm	1.0×1016
	13	Dielectric intensity	GB/T 1693-2007	Kv/mm(25ºC)	18~25
	14	Temperature Resistance	Measured	ºC	-50~+250

* UV-94 Fire retardant: After two times 10s burn tests on a 3mm-thick sample, the flame was extinguished within 30s, and no burnt fell. [1]

* Noted: The data after curing are all measured after the silicone is completely cured.

Product Feature

Good Thermal conductivity；Flame retardant, high and low -temperature resistance
No corrosion of potting components after curing; Flexible

PACKING

10KG / Set (A, 5kg + B, 5kg)

20KG / Set (A, 10kg + B, 10kg)

50KG / Set (A, 25kg + B, 25kg)

- Storage and transportation:

This product is non-toxic non-dangerous goods, according to the general chemical handling, stored in a cool & dry place (room temperature).

- Shelf Life: 6 months, overdue please reinspect; If it meets the standard, it can still be used.

55 Shore A cured Silicone Potting Compound Glue Adhesive 1:1 2 Parts 0

Tags:

silicone potting gel

rubber potting compound

rtv potting

2 Part Clear RTV Silicone Potting Compound Material Insulation Waterproof 10:1

Get Best Price

Video

Thermal Conductivity Electronic Potting Silicone Liquid Two Component Custom

Get Best Price

Video

Moisture Proof AB Silicone Potting Compound Rubber Raw Material For Electronic Appliances

Get Best Price

Video

Waterproof RTV Potting Compound Silicone Gel Material High Thermal Conductivity

Get Best Price

Video