建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性

建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性

ブランド名: Hnanast
モデル番号: HN-620
Moq: 1kg
価格: 5.85-6.88$
パッケージの詳細: 25kg
支払条件: L/C,D/A,D/P,T/T,Western Union
詳細情報
Place of Origin:
China
Features:
low shrinkage
Usage:
mold making
Shape:
Liquid Two Component
Package:
20kg/25kg
Operating Temperature:
-50°C to 200°C
Shrinkage Rate:
less than 0.2%
Feature:
High tensile resistance,
Goods Description:
Silicone in primary forms
Mixed Viscosity:
20000~24000 Cps
Shelf Life:
12 months
Specific Gravity:
1.08
Type:
tin cure silicone rubber
Elongation Break:
450-500 %
Tensile Strength:
6 MPa
Application:
Mold making, casting, prototyping
Enlogation:
600%
Curing Time:
24 hours
Working Time:
30~40mins
Working Temperature:
-50℃ to 200℃
Description:
Silicone in primary forms
Appearance:
Liquid
Shrinkage:
≤0.3%
Elongation At Break:
400%
Wokring Time:
30-40 min
Sample:
1kg silicone sample for free
Curing Agent:
Tin Catalyst CA30
Grade:
molding
Supply Ability:
100ton/mouths
ハイライト:

高強度スチール硬化型LSR

,

耐久性のある建築模具シリコン

,

費用対効果の高いチンの硬化ゴム

製品説明


工業用品のための最適化された技術紹介

シリコンゴム (LSR)

建築 模具 の 製造 に 役立つ 優れた 材料
 
RTV-2のチンの硬化液体シリコンゴム (LSR) は,コンクリート,石膏,シリコンベースの建築部品のための高耐久性模具の製造において例外的な性能を提供します.精度と耐久性のために設計された壁のタイル,装飾されたローマの柱,複雑なリレフパネルなどの装飾要素を製造するのに最適な選択です
 

建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性 0


硬化されたスチール製のLSRの主要特性
1超低収縮率 (<0.2%)
- 硬化後の変形なく細かい表面質感 (石粒,花のモチーフなど) の寸法安定性と正確な複製を保証する.
- 縫い目のない組み立てを必要とする大規模モジュール型模具にとって重要です
 
2涙耐性と熱安定性が向上しました
- 200°Cの加工温度に耐えるため,熱固化コンクリートとジプスと互換性があります
- 頑丈な機械特性により,脱模の際に模具の損傷を軽減し,従来のゴムと比較して使用寿命を30~50%延長します.
 
3. 厳しい環境における化学的惰性
- アルカリ (pH12+),酸,湿度に耐性がある 屋外用途やポートランドセメントのような化学的に攻撃的な基板に最適
- 発泡剤や清掃剤による分解を防ぐ
 
4大量生産のためのコスト効率
- プラチナ製のLSRよりも材料コストが40~60%低くなって,非医療用には細部精度が同等である.
- 室温固化により,製造におけるエネルギー消費量が減少します.
 
建築用模具製造における応用

- プリファブリック建築要素:GFRCファサードのための再利用型模具,文化遺産復元
- 景観 硬化: 舗装 バルストラード 偽造石のファニヤーの高サイクル生産
- DIY/職人用:最小限の装備で小批量職人用には使いやすい.
  

良い価格  オンライン

商品の詳細

家へ > 製品 >
錫の治療のシリコーン ゴム
>
建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性

建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性

ブランド名: Hnanast
モデル番号: HN-620
Moq: 1kg
価格: 5.85-6.88$
パッケージの詳細: 25kg
支払条件: L/C,D/A,D/P,T/T,Western Union
詳細情報
Place of Origin:
China
ブランド名:
Hnanast
Model Number:
HN-620
Features:
low shrinkage
Usage:
mold making
Shape:
Liquid Two Component
Package:
20kg/25kg
Operating Temperature:
-50°C to 200°C
Shrinkage Rate:
less than 0.2%
Feature:
High tensile resistance,
Goods Description:
Silicone in primary forms
Mixed Viscosity:
20000~24000 Cps
Shelf Life:
12 months
Specific Gravity:
1.08
Type:
tin cure silicone rubber
Elongation Break:
450-500 %
Tensile Strength:
6 MPa
Application:
Mold making, casting, prototyping
Enlogation:
600%
Curing Time:
24 hours
Working Time:
30~40mins
Working Temperature:
-50℃ to 200℃
Description:
Silicone in primary forms
Appearance:
Liquid
Shrinkage:
≤0.3%
Elongation At Break:
400%
Wokring Time:
30-40 min
Sample:
1kg silicone sample for free
Curing Agent:
Tin Catalyst CA30
Grade:
molding
Minimum Order Quantity:
1kg
価格:
5.85-6.88$
Packaging Details:
25kg
Delivery Time:
5-10day
Payment Terms:
L/C,D/A,D/P,T/T,Western Union
Supply Ability:
100ton/mouths
ハイライト:

高強度スチール硬化型LSR

,

耐久性のある建築模具シリコン

,

費用対効果の高いチンの硬化ゴム

製品説明


工業用品のための最適化された技術紹介

シリコンゴム (LSR)

建築 模具 の 製造 に 役立つ 優れた 材料
 
RTV-2のチンの硬化液体シリコンゴム (LSR) は,コンクリート,石膏,シリコンベースの建築部品のための高耐久性模具の製造において例外的な性能を提供します.精度と耐久性のために設計された壁のタイル,装飾されたローマの柱,複雑なリレフパネルなどの装飾要素を製造するのに最適な選択です
 

建築用模具のための高強度チンの硬化LSR 耐久性・コスト効率性 0


硬化されたスチール製のLSRの主要特性
1超低収縮率 (<0.2%)
- 硬化後の変形なく細かい表面質感 (石粒,花のモチーフなど) の寸法安定性と正確な複製を保証する.
- 縫い目のない組み立てを必要とする大規模モジュール型模具にとって重要です
 
2涙耐性と熱安定性が向上しました
- 200°Cの加工温度に耐えるため,熱固化コンクリートとジプスと互換性があります
- 頑丈な機械特性により,脱模の際に模具の損傷を軽減し,従来のゴムと比較して使用寿命を30~50%延長します.
 
3. 厳しい環境における化学的惰性
- アルカリ (pH12+),酸,湿度に耐性がある 屋外用途やポートランドセメントのような化学的に攻撃的な基板に最適
- 発泡剤や清掃剤による分解を防ぐ
 
4大量生産のためのコスト効率
- プラチナ製のLSRよりも材料コストが40~60%低くなって,非医療用には細部精度が同等である.
- 室温固化により,製造におけるエネルギー消費量が減少します.
 
建築用模具製造における応用

- プリファブリック建築要素:GFRCファサードのための再利用型模具,文化遺産復元
- 景観 硬化: 舗装 バルストラード 偽造石のファニヤーの高サイクル生産
- DIY/職人用:最小限の装備で小批量職人用には使いやすい.