Two Components Silicone For Encapsulation Of Elec 1:1 Silicone Potting Compound For Inverter EV Battery Adapter Charger High Thermal Conductivity
Product description:
Silicone potting compound is a soft, flexible silicone elastomer specifically designed for encapsulating and protecting electronic components. It is typically supplied as two-component liquids that cure at room or elevated temperatures. This material provides excellent electrical insulation, shock resistance, and protection against moisture, chemicals, and thermal cycling, ensuring long-term reliability for sensitive electronics in various applications.
| Test Items | Test Standard | Units | Product test results | |||
| Part A | Part B | |||||
|
Before Curing
|
1 | Appearance | By eyes | --- | Grey, fluid | White, fluid |
| 2 | Viscosity | GB/T10247- 2008 | 25ºC,mPa·S | 4500~5000 | 4500~5000 | |
| 3 | Density | GB/T 13354-92 | 25ºC,g/cm3 | 1.50±0.05 | 1.50±0.05 | |
| 4 | Mixing Ratio (A : B) | 1:1 | Weight ratio | 100 | 100 | |
| Volume ratio | 100 | 100 | ||||
| 5 | Operating time | Measured | hr | 0.3-0.4 | ||
| 6 | Curing condition | Measured | hr |
4~12 (25ºC, initial cure) |
||
|
0.20 (80ºC) |
||||||
|
After Curing
|
7 | Appearance | By eyes | --- | Grey Elastomer | |
| 8 | Hardness | GB/T 531.1-2008 | Shore A | 50±5 | ||
| 9 | Thermal conductivity | GB/T10297-1998 | w/m·k | ≥0.76 | ||
| 10 | Expansivity | GB/T20673-2006 | µm/(m,ºC) | 210 | ||
| 11 | Moisture Absorption | GB/T 8810-2005 | 24h,25ºC,% | 0.01~0.02 | ||
| 12 | Volume resistivity | GB/T 1692-92 | (DC500V),Ω· cm | 1.0×1016 | ||
| 13 | Dielectric intensity | GB/T 1693-2007 | Kv/mm(25ºC) | 18~25 | ||
| 14 | Temperature Resistance | Measured | ºC | -50~+250 | ||
- Storage and transportation:
This product is non-toxic non-dangerous goods, according to the general chemical handling, stored in a cool & dry place (room temperature).
- Shelf Life: 6 months, overdue please reinspect; If it meets the standard, it can still be used.