Hardness Customized Black Epoxy Potting Compound 5:1 Fire Retardant High Temp Potting Epoxy Resin For Automobile Motorcycle Ignition LED Driver Power Supply 2 Parts Electronic Potting Glue
Product Description:
HN-5508 epoxy resin at room temperature or low temperature, with low viscosity, long operation time, good fluidity, and easy penetration into the clearance of the product; no bubbles after curing, smooth surface, luster, high hardness
technical parameter
| uring |
builder |
Epoxy resin 5508 |
Curing agent 5508 |
| pigment |
Black / White et al |
Ruburn / transparent surface |
| |
A sticky epoxy resin water |
r liquid specific |
| c gravity, g / cm3 |
1.4-1.5 |
1.05 |
| Viscosity of 25℃ |
4,500—6,000cp s |
150—250cp storage |
| e Period (25℃) |
Six months |
x months |
|
processabili
|
mixing ratio |
A: B =5:1 (weight ratio) |
| Available for a time of 25℃ |
2-3H (100g mix) |
| curing time |
25℃ / 6-8H surface stem, 12-16H fully cured or 60-80℃/1.5-2H |
| After curing |
2 Tensile strength of kg/cm |
16-18 |
| 2 Compressive strength of kg/cm |
18-22 |
| Resistance to the voltage of kv/mm |
20-22 |
| Surface resistance ofΩ-cm |
14
1.2*10
|
| Volume resistance ofΩ-cm |
15
1.1*10
|
| contraction percentage% |
0.35-0.55 |
| Water absorption rate was 25℃ * 24H |
<0.03% |
| The hardness of SHORE A |
85-95 |
|
distortion
temperature ℃
|
130-150 |
| low temperature resistant ℃ |
-30 |
Product Application:
HN-5508 is widely used in transformers, resistors, filters, temperature sensors, temperature controllers, ignition coils, high voltage packs, aquarium equipment, anion generators, ultrasonic atomizers
Matters need attention:
1. This product is an AB agent, according to the label ratio on the product package, and the mixing ratio is weight ratio and non-volume ratio.
2, AB agent mixing can not be stirred with a round bar without resistance, must be stirred with a flat tool with resistance, it is best to use a small mixer.
3. This product should be placed in a cool and dry place to avoid light, keep the workshop dust-free, and cover the unused glue after opening the lid in time.
4. The performance test data is the test result when the humidity is 60% and the temperature is 25℃, for customer reference only.
5, resin glue stored in a wet environment will exhibit a crystallization phenomenon, please put it in the oven at a low temperature hot dry, and restore its original state.